Reliability analysis for anchorage of reinforced concrete beamswith longitudinal cracks due to corrosion at anchorage zone(
)
钢筋混凝土简支梁锚固区锈胀开裂后锚固可靠度分析
)Journal of Southeast University (English Edition)[ISSN:1003-7985/CN:32-1325/N]
- Volumn:
- 21
- Issue:
- 2005 3
- Page:
- 336-341
- Research Field:
- Civil Engineering
- Publishing date:
- 2005-09-30
Info
- Title:
- Reliability analysis for anchorage of reinforced concrete beamswith longitudinal cracks due to corrosion at anchorage zone
- 钢筋混凝土简支梁锚固区锈胀开裂后锚固可靠度分析
- Author(s):
- Shi Bo; Zhao Guofan
- School of Civil and Hydraulic Engineering, Dalian University of Technology, Dalian 116023, China
- Keywords:
- reinforcement corrosion; bond behavior; anchorage; reinforced concrete structure; corrosion-induced crack
- PACS:
- TU311.2
- DOI:
- 10.3969/j.issn.1003-7985.2005.03.018
- Abstract:
- An anchorage reliability analysis approach for simply supported reinforced concrete beams under corrosion attack in the anchorage zone is developed.The first-order second-moment method is employed to analyze the effects of various factors on the anchorage reliability.These factors include both the length and width of cover cracking due to reinforcement corrosion, the cover thickness, the anchorage length, and the stirrup ratio.The results show that the effect of corrosion-induced crack length on the reliability index for anchorage, β0, is negligible when the crack on the concrete surface is just appearing, but with the crack widening, the β0 value is reduced significantly;the considerable changes in β0 result from a variation in cover depth and anchorage length;the effect of changes in the diameter or space of stirrups on the anchorage resistance is very limited, and the variation in β0 is also very low.
- 为了研究锚固区混凝土锈胀开裂后构件的锚固可靠度的变化情况, 采用一次二阶矩方法分析了锈胀裂缝的长度及宽度、保护层厚度、钢筋锚固长度以及配箍率等参数对混凝土简支梁锚固可靠度的影响.分析结果表明:当保护层刚开裂时, 锈胀裂缝长度对锚固可靠指标β0的影响很小, 此后, 随着裂缝宽度的增加, β0有了明显的降低;保护层厚度和锚固长度的变化对β0有相当大的影响;改变箍筋的直径或间距对锚固抗力的影响很小, 因此, β0变化的幅度也很小.
References:
[1] Cabrera J G.Deterioration of concrete due to reinforcement steel corrosion [J].Cement & Concrete Composites, 1996, 18(1):47-59.
[2] Yuan Yingshu, Jia Fuping, Cai Yue.The structural behavior deterioration model for corroded reinforced concrete beams [J].China Civil Engineering Journal, 2001, 34(3):47-52.(in Chinese)
[3] Fan Yingfang, Zhou Jing, Huang Zhenguo.Experimental research on strength of R.C.member corroded by chloride [J].Industrial Construction, 2001, 31(5):3-5.(in Chinese)
[4] Shao Zhuomin, Shen Wendu, Xu Youlin.The reliability and design for anchorage of reinforcing bars [J].Journal of Building Structures, 1987, 8(4):36-49.(in Chinese)
[5] Xu Youlin, Shen Wendu, Wang Hong.An experimental study of bond-anchorage properties of bars in concrete [J].Journal of Building Structures, 1994, 15(3):26-37.(in Chinese)
[6] Wang Linke, Tao Feng, Wang Qinglin, et al.Experimental study on bond and anchorage of corroded reinforcement in concrete [J].Industrial Construction, 1996, 26(4):14-16.(in Chinese)
[7] Zhang Weiping, Zhang Yu.Test study on deterioration model of bond behavior between corroded reinforcement and concrete [J].Building Structure, 2002, 32(1):31-33.(in Chinese)
[8] Shao Zhuomin, Xu Youlin.The study and design proposition for bond-anchorage of reinforced concrete [J].Building Structure, 1986, 16(4):2-12.(in Chinese)
[9] China Highway Planning and Design Institute. GB/T 50283—1999 Unified standard for reliability design of highway engineering structures [S].Beijing: China Planning Press, 1999.(in Chinese)
[10] Al-Sulaimani G J, Kaleemullah M, Basunbul L A, et al.Influence of corrosion and cracking on bond behavior and strength of reinforced concrete members [J].ACI Structural Journal, 1990, 87(2):220-231.
Memo
- Memo:
- Biographies: Shi Bo(1971—), male, graduate;Zhao Guofan(corresponding author), male, professor, academician of Chinese Academy of Engineering, zhaogf@dlut.edu.cn.